Description
PLA Marble Filament by ELEGOO
Marble-colored filament from ELEGOO allows you to create unique models with a realistic stone finish. Thanks to additives that give the surface the characteristic marble effect, the prints gain an aesthetic that is ideal for decorations, figurines or architectural mock-ups. The material is based on PLA (polylactide - a plant-based biodegradable plastic), so it is environmentally friendly. There is 1 kg of filament on the spool, which is enough for many medium and large prints.
Stable and clean printing
The product has a diameter of 1.75 mm and a very precise dimensional tolerance (± 0.02 mm), which ensures even feeding into the printer without jams. It adheres well to the work table and does not create bubbles or excessive threads (known as stringing), which minimizes material waste and saves time. The result is smooth, durable models with a uniform appearance.
Practical and eco-friendly spools
Filament spools are made of cardboard, making it easy to recycle and reducing the product's environmental impact. In addition, each spool is precisely wound by machine and controlled by hand to prevent tangling. Three holes in the spool make it easy to see how much material is left.
General
| Manufacturer |
ELEGOO |
| Model |
50.203.0113 |
| Color |
Marble |
| Weight |
1 kg |
Recommended print settings
| Drying settings before printing |
55 ± 5°C |
| Ambient temperature and humidity |
≤ 50°C, ≤ 20% relative humidity (store with moisture absorber) |
| Nozzle temperature |
190 - 230°C |
| Table temperature (depending on printer and surface) |
35 - 65°C |
| Type of working surface |
Textured PEI (polyetherimide - a durable, adherent material used as a base for 3D printing) or other compatible surface |
| Printing speed |
Less than 300 mm/s |
Physical properties
| Density |
1.26 g/cm³ |
| Melting point |
158°C |
| Deflection temperature under load |
57°C |
| Softening temperature (Vicat test) |
62°C |
Mechanical properties
| Tensile strength (XY-measurement made in the horizontal plane of the print, where the material is strongest) |
38 ± 3 MPa |
| Elongation at break (XY) |
10,5% ± 2,1% |
| Bending strength (XY) |
72 ± 5 MPa |
| Bending modulus (XY) |
2993 ± 182 MPa |
| Impact strength (XY) |
66.2 ± 3.9 kJ/m² |